Compression Bonded Moulded NdFeB Magnet

Compression bonded magnets are composed of a special form of NdFeB powder with adhesive and using compression molding techniques in simple tools, it can be quickly machined into complex shapes. Since its materials are isotropic, bonded NdFeB magnet can be magnetized in any direction or with multiple poles. Special magnetizing fixtures are required in order to achieve multiple poles magnetization, depending on complexity of design and production. Compression Bonded Moulded NdFeB Magnet

Compression Bonded Moulded NdFeB Magnet

Compression Bonded Moulded NdFeB Magnet

Application Areas

Mould injection NdFeB have various application areas such as:
Excellent mechanical strength and surface finish.
Compression molded magnets can be manufactured to very tight tolerances.
Greater cracking and chipping resistance than other rare earth magnets.
Superior energy to weight ratio.
Can be molded into a variety of shapes and sizes.
Magnetic values up to 10 MGOe.

The energy product is 3 times as large as anisotropic ferrite. The intrinsic coercive force is high. During the large-scale production, the magnetic properties are stable and conformity is good.
Single-time molding and multi-poles orientation.
Low tooling cost.
Co-injected assemblies.
Effective surface treatment to prevent corrosion.
Widely applied in all kinds of mini-motors, auto motors, air-conditioner motors, automatic controlling devices, sensors, drivers, telecom and instrument industry.
Stable working temperature: It can be high up to 150℃.

Bonded Compression NdFeB Typical Magnetic Properties
Grade Properties Remanence
Br
T(Gs)
Coercivity
HCB KA/m(KOe)
Intrinsic Coercivity
Hcj
KA/m(Koe)
Max. Energy
Product
BH(max)
KJ/m3 (MGOe)
Density
g/cm3
Relative Recoil
Permeability
µr
Temperature Coefficient
of RemanenceαBr %/ ℃
Max Operating
Temperature Tw℃
BNP-6 0.55~0.62 285~370
(3.6~4.6)
600~755
(7.5~9.5)
44~56
(5.5~7.0)
5.5~6.1 1.15 -0.13 100
BNP-8L 0.60~0.64 360~400
(4.5~5.0)
715~800
(9~10)
56~64
(7.0~8.0)
5.6~6.1 1.15 -0.13 100
BNP-8 0.62~0.69 385~445
(4.8~5.6)
640~800
(8~10)
64~72
(8.0~9.0)
5.6~6.1 1.15 -0.13 120
BNP-8SR 0.62~0.66 410~465
(5.2~5.8)
880~1120
(11~14)
64~72
(8.0~9.0)
5.6~6.1 1.13 -0.13 150
BNP-8H 0.61~0.65 410~445
(5.2~5.7)
1190~1440
(15~18)
64~72
(8.0~9.0)
5.9~6.2 1.15 -0.07 125
BNP-9 0.65~0.70 400~440
(5.0~5.5)
640~800
(8~10)
70~76
(8.8~9.5)
5.6~6.1 1.22 -0.12 120
BNP-10 0.68~0.72 420~470
(5.3~5.9)
640~800
(8~10)
76~84
(9.5~10.5)
5.6~6.1 1.22 -0.11 120
BNP-11 0.70~0.74 445~480
(5.6~6.0)
680~800
(8.5~10)
80~88
(10~11)
5.6~6.1 1.22 -0.11 120
BNP-11L 0.70~0.74 400~440
(5.0~5.5)
520~640
(6.5~8)
78~84
(9.8~10.5)
5.6~6.1 1.26 -0.11 110
BNP-12L 0.74~0.80 420~455
(5.3~5.7)
520~600
(6.5~7.5)
84~92
(10.5~11.5)
5.6~6.1 1.26 -0.08 110

Diametrically Magnetization Compression Bonded Magnet Ring

Segment Neodymium Compression Bonded Magnet

Segment Neodymium Compression Bonded Magnet

Epoxy Coating Ring Compression Bonded NdFeB Rotor Magnets W/ 8 Poles

Thin Thickness Compression Bonded Radial Ring Magnets